TECHNICAL DATA SHEET|
XTRACON LM ALLOY 201-30
Xtracon LM Alloy 201-30 is a modified polyether urethane
elastomer alloy designed for extrusion and injection molding.
The material contains 30% of a proprietary ETP and is
characterized by much wider process temperature profile
and rapid set-up speed while maintaining excellent low
temperature flexibility and the highly elastic nature
of the base polyurethane. The material has excellent
resistance to moisture and abrasion and would be an excellent
candidate for wire and cable jacketing. LM ALLOY 201-30
exhibits minimal stress whitening and very high tensile elongation.
psi @ 25°C
|10 - 15,000|
|Shore A||80 - 85|
|Melt Flow Index|
190°C, 8.7 Kg. Load
10 Min, Gms.
|7 - 9|
|Tensile Strength, psi||4290|
|Elongation @ Break, psi||875|
|Water Content ( % )||0.03|
XTRACON LM ALLOY 201-30 should be stored in a cool dry place and
care should be taken to re-seal containers carefully that have been
opened to avoid contamination by atmospheric moisture.
XTRACON LM ALLOY 201-30 is not considered to be hazardous
under SARA TITLE III. Safe industrial handling and hygiene
practices are always highly recommended. Polyurethanes and
other plastics produced with this product my present a fire
hazard in certain applications if exposed to fire and/or
excessive heat, e.g. welding and cutting torches in the presence
of oxygen or air. Refer to MSDS for more information.
XTRACON LM ALLOY 201-30 is available in 50 lb. bags, 1000 lb.
pallets (20 bags- shrink-wrapped) or 1000 lb. Gaylord containers.
The facts stated and recommendations made herein are based
on our research and research of others, and are believed
to be accurate. No guarantee of their accuracy is made, however,
and the product discussed is recommended without warranty on our part,
express or implied, and upon conditions that recipients shall
make their own test to determine its suitability for their purposes.
Likewise, statements concerning the possible uses of the product
are not intended as recommendations to use it in the infringement
of any patent.