TECHNICAL DATA SHEET|
XTRACON LM ALLOY 201-40
Xtracon LM Alloy 201-40 is a modified polyether urethane elastomer
alloy designed for extrusion and injection molding.
The material contains 40% of a proprietary ETP and is
characterized by much wider process temperature profile
and rapid set-up speed while maintaining excellent low
temperature flexibility and the highly elastic nature of
the base polyurethane. The material has excellent resistance
to moisture and abrasion and would be an excellent candidate
for wire and cable jacketing. LM ALLOY 201-40 exhibits minimal
stress whitening and very high tensile elongation.
psi @ 25°C
|12 - 16,000|
|Shore A||82 - 86|
|Melt Flow Index|
190°C, 8.7 Kg. Load
10 Min, Gms.
|2 - 4|
|Tensile Strength, psi||4000|
|Elongation @ Break, psi||770|
|Water Content ( % )||0.03|
XTRACON LM ALLOY 201-40 should be stored in a cool dry place
and care should be taken to re-seal containers carefully that
have been opened to avoid contamination by atmospheric moisture.
XTRACON LM ALLOY 201-40 is not considered to be hazardous under
SARA TITLE III. Safe industrial handling and hygiene practices are
always highly recommended. Polyurethanes and other plastics produced
with this product my present a fire hazard in certain applications
if exposed to fire and/or excessive heat, e.g. welding and cutting
torches in the presence of oxygen or air.
Refer to MSDS for more information.
XTRACON LM ALLOY 201-40 is available in 50 lb. bags,
1000 lb. pallets (20 bags- shrink-wrapped) or 1000 lb. Gaylord containers.
The facts stated and recommendations made herein are based
on our research and research of others, and are believed
to be accurate. No guarantee of their accuracy is made, however,
and the product discussed is recommended without warranty on our part,
express or implied, and upon conditions that recipients shall
make their own test to determine its suitability for their purposes.
Likewise, statements concerning the possible uses of the product
are not intended as recommendations to use it in the infringement
of any patent.